| 配方類型： |
POLISH |
| 配方說明： |
Acid-Removable Wax Floor Polish |
| 配方組成： |
"Carbitol/4.0
Cationi
FC-134 or 128 (1% Solution)/.5
"Igepal" CO-610/-
"NeoCryl" A-400 or A-410 (15%)/55.0
Wax Emulsion (15%)/35.0
Tributoxyethyl Phosphate/1.0
Alkali-Soluble Resin Emulsion (15%)/10.0
"Carbitol/2.0
Tributoxyethyl Phosphate/1.0
FC-134 or 128 (1% Solution)/.5
"Igepal" CO-610/-
FC-134 or 128 (1% Solution)/.5
Polyethylene/11.8 Parts
"Renex" 690/3.0
"Duomeen" T/-
Oleic Acid/-
Morpholine/-
KOH (60%)/0.3
|
| 配制方法： |
The wax and emulsifiers (or oleic acid) are melted together at 240F. The aqueous KOH, morpholine, or acetic acid is then added slowly.
The hot melt at 240F-250F is then added slowly to water heated to 200F-210F with suitable agitation, so that the wax is immediately dispersed.
The alkali-soluble resin solution can be prepared by conventional methods. "Shanco" 334, "Durez" 19788, "Schenectady" SR-88 and shellac are recommended.
In making the final blend, the wax emulsion followed by the alkali-soluble resin solution can be added either to the "NeoCryl" at 15% solids or to 40% "NeoCryl" with water of dilution being added afterwards. The tributoxyethyl phosphate and fluorocarbon should be incorporated as the next step and finally the pH should be adjusted to 9.5, usually with ammonia.
Formulas No.1 through 4 are very hard and durable and can be considered non-buffable. No.5 is slightly buffable and No.6 and No.7 are moderately buffable: the Nos. 5, 6, and 7 are extremely tough and resist |
|