| 配方類型： |
CEMENT AND RELATED PRODUCTS |
| 配方說明： |
Caulking Compounds |
| 配方組成： |
Talc/3.50 or 100.00 % by Wt
The caulk was mixed in a sigma blade mixer. "Indopol" Polybutene,
butyl rubber solution and drying oil were added and mixed well (5-10
minutes). Then the fillers were slowly added to the mixing vehicle in
the order shown above. After the addition of titanium-calcium pigment,
the mass was mixed to a smooth paste (about 35 minutes). the drier was
added along with sufficient mineral spirits to obtain the desired
consistency. Mixing was continued un |
| 配制方法： |
The caulk was mixed in a sigma blade mixer. INDOPOL Polybutene and drying oil were added and mixed well (5-10 minutes). Then the fillers were slowly added to the mixing vehicle in the order shown above. After the addition of titanium-calcium pigment, the mass was mixed to a smooth paste (about 35 minutes). the drier was added along with sufficient mineral spirits to obtain the desired consistency. Mixing was continued until the mass was uniform (about 3-5 minutes). |
|